Measuring attrition resistance of oxygen carrier particles for chemical looping combustion with a customized jet cup

Magnus Rydén (Institutionen för energi och miljö, Energiteknik) ; Patrick Moldenhauer (Institutionen för energi och miljö, Energiteknik) ; Simon Lindqvist (Institutionen för energi och miljö, Energiteknik) ; Tobias Mattisson (Institutionen för energi och miljö, Energiteknik) ; Anders Lyngfelt (Institutionen för energi och miljö, Energiteknik)
Powder Technology (0032-5910). Vol. 256 (2014), p. 75-86.
[Artikel, refereegranskad vetenskaplig]

A customized jet cup for measuring attrition resistance of oxygen carrier particles for chemical looping combustion has been constructed and used to evaluate 25 different material samples, all of which previously have been subject to continuous operation in chemical looping reactors at Chalmers University of Technology. The effect of continuous operation has been assessed by comparing attrition behavior of fresh particles with that of used ones. It is concluded that the correlation between the jet cup tests and operational experience is robust, and that there is always considerable difference in attrition resistance between fresh and used particles of the same batch. Composite materials with NiO or Fe2O3 as active phase and Al2O3-, NiAl2O4- or MgAl2O4-based support and materials based on the CaMnO3-δ perovskite structure typically had high attrition resistance, which improved further following operation with fuel. Combined (FexMn1-x)2O3 oxides and all materials containing smaller or larger amounts of either CuO or ZrO2 experienced reduced attrition resistance during operation with fuel, and usually also had low attrition resistance to begin with. Fresh particles of the commonly used oxygen carrier ilmenite had reasonably high attrition resistance, while ilmenite that had been subject to chemical looping combustion of natural gas showed higher rate of attrition. No strong correlation between the commonly used crushing strength index and attrition resistance measured with jet cup could be established, but it was clear that particles with a crushing strength above 2N were much more likely to have high attrition resistance compared to softer particles. As compared to crushing strength, the jet cup testing was better correlated to attrition in actual operation.

Nyckelord: Attrition, Chemical looping combustion, Chemical looping reforming, Fluidization, Jet cup, Oxygen carrier particles

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2014-03-26. Senast ändrad 2016-04-28.
CPL Pubid: 195693


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för energi och miljö, Energiteknik (2005-2017)


Hållbar utveckling
Kemisk energiteknik
Övrig bearbetning/sammanfogning

Chalmers infrastruktur