Modeling wood fiber deformation caused by vapor expansion during steam explosion of wood

Muhammad Muzamal (Institutionen för kemi- och bioteknik, Kemisk reaktionsteknik) ; E. K. Gamstedt ; Anders Rasmuson (Institutionen för kemi- och bioteknik, Kemisk apparatteknik)
Wood Science and Technology (0043-7719). Vol. 48 (2014), 2, p. 353-372.
[Artikel, refereegranskad vetenskaplig]

Steam explosion is a process used to enhance enzyme penetration and digestibility of wood. Wood chips are processed with high-pressure steam for a limited time, and the bonding between polysaccharides and lignin is weakened. After this processing, the pressure is rapidly reduced to induce steam explosion where the vapor inside a fiber expands and exerts pressure on the fiber walls. This pressure causes fiber deformation and breakage. In this study, fiber deformation caused by vapor expansion was simulated by single wood fibers using finite element modeling. When pressure is applied inside a fiber, it is likely to break from the corner and midway between two adjacent corners. The fiber is modeled with four layers (P, S1, S2, and S3). Although the P, S1, and S3 layers are very thin, they significantly prevent fiber deformation. The fibers with a thin wall and a low micro-fibril angle (MFA) deform more than the fibers with a thick wall and a higher MFA. It was found that the shape of the fiber plays an important role in its deformation. The areas of localized strain are the most likely places for fiber splitting. Essentially, fiber wall damage is more likely to occur in (1) thin-walled fibers, i.e., earlywood, (2) fibers with damaged P and S1 layers, (3) fibers with low MFAs, and (4) fibers with irregular cross-sections. Different chemical pretreatments, fractionation procedures, and selections of raw materials can accordingly be considered to produce easily steam-exploded materials.


Denna post skapades 2014-03-21. Senast ändrad 2015-12-17.
CPL Pubid: 195373


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för kemi- och bioteknik, Kemisk reaktionsteknik (2005-2014)
Institutionen för kemi- och bioteknik, Kemisk apparatteknik (2005-2014)


Pappers-, massa- och fiberteknik

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:

Structural Modifications in Spruce Wood during Steam Explosion Pretreatment