Characterisation of structure and conductivity of BaTi0.5Sc 0.5O3 - δ

Seikh Rahman (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Istaq Ahmed (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Reider. Haugsrud ; Sten G. Eriksson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Christopher S Knee (Institutionen för kemi- och bioteknik, Oorganisk miljökemi)
Solid State Ionics (0167-2738). Vol. 255 (2014), p. 140-146.
[Artikel, refereegranskad vetenskaplig]

BaTi0.5Sc0.5O3 - δ was prepared via solid state reaction route and final sintering at 1550 C. High resolution X-ray powder diffraction on the as-prepared material reveals a cubic perovskite structure with a unit cell parameter, a = 4.1343(1) Å. Thermogravimetric analysis revealed the presence of significant levels of protons in the as-prepared material and 74% of the theoretically achievable protonation through filling of oxide ion vacancies was attained on exposure to a humid environment at 185 C. Infrared spectroscopy revealed a broad OH stretching band confirming the presence of OHO • defects. Electrical conductivity was measured with variable frequency AC impedance methods in oxygen, argon, and hydrogen under dry, hydrated (H2O) and heavy water (D2O) conditions. In the temperature range of 150-550 C in a wet gas atmosphere the conductivity is significantly higher than that observed for dry conditions, indicating that protons are the dominant charge carriers. Conductivity is also found to be higher in dry oxygen in comparison with dry argon over the whole temperature range of 150-1000 C, characteristic of contribution from p-type charge carriers under oxidising atmospheres. At 550 C the proton conductivity was estimated to be 2.89 × 10- 4 S cm- 1 in wet Ar. Fitting of conductivity data provides a hydration enthalpy change (ΔH hydr 0) of - 100 ± 5 kJ/mol and hydration entropy change (ΔShydr 0) of - 160 ± 10 J/mol K.

Nyckelord: Barium titanate , BaTiO3 , Hydration , Perovskite , Proton conductivity , X-ray diffraction

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2014-02-28. Senast ändrad 2016-08-15.
CPL Pubid: 194297


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för kemi- och bioteknik, Oorganisk miljökemi (2005-2014)


Building Futures
Hållbar utveckling

Chalmers infrastruktur