Microstructure of Haynes® 282® Superalloy after Vacuum Induction Melting and Investment Casting of Thin-Walled Components

Hubert Matysiak ; Malgorzata Zagorska ; Joel Andersson (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Alicja Balkowiec ; Rafal Cygan ; Marcin Rasinski ; Marcin Pisarek ; Mariusz Andrzejczuk ; Krzysztof Kubiak ; Krzysztof J. Kurzydlowski
Materials Vol. 6 (2013), 11, p. 5016-5037.
[Artikel, refereegranskad vetenskaplig]

Abstract: The aim of this work was to characterize the microstructure of the as-cast Haynes® 282® alloy. Observations and analyses were carried out using techniques such as X-ray diffraction (XRD), light microscopy (LM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray spectroscopy (EDS), wave length dispersive X-ray spectroscopy (WDS), auger electron spectroscopy (AES) and electron energy-loss spectrometry (EELS). The phases identified in the as-cast alloy include: γ (gamma matrix), γʹ (matrix strengthening phase), (TiMoCr)C (primary carbide), TiN (primary nitride), σ (sigma-TCP phase), (TiMo)2SC (carbosulphide) and a lamellar constituent consisting of molybdenum and chromium rich secondary carbide phase together with γ phase. Within the dendrites the γʹ appears mostly in the form of spherical, nanometric precipitates (74 nm), while coarser (113 nm) cubic γʹ precipitates are present in the interdendritic areas. Volume fraction content of the γʹ precipitates in the dendrites and interdendritic areas are 9.6% and 8.5%, respectively. Primary nitrides metallic nitrides (MN), are homogeneously dispersed in the as-cast microstructure, while primary carbides metallic carbides (MC), preferentially precipitate in interdendritic areas. Such preference is also observed in the case of globular σ phase. Lamellar constituents characterized as secondary carbides/γ phases were together with (TiMo)2SC phase always observed adjacent to σ phase precipitates. Crystallographic relations were established in-between the MC, σ, secondary carbides and γ/γʹ matrix.

Nyckelord: Haynes® 282®; vacuum induction melting; investment casting; superalloy; microstructure

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2013-12-19. Senast ändrad 2016-07-13.
CPL Pubid: 190003


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)


Hållbar utveckling
Metallurgisk process- och produktionsteknik
Funktionella material

Chalmers infrastruktur