Effect of Molecular Composition of Heparin and Cellulose Sulfate on Multilayer Formation and Cell Response

N. Aggarwal ; Noomi Altgärde (Institutionen för teknisk fysik, Biologisk fysik) ; Sofia Svedhem (Institutionen för teknisk fysik, Biologisk fysik) ; K. Zhang ; S. Fischer ; T. Groth
Langmuir (0743-7463). Vol. 29 (2013), 45, p. 13853-13864.
[Artikel, refereegranskad vetenskaplig]

Here, the layer-by-layer method was applied to assemble films from chitosan paired with either heparin or a semisynthetic cellulose sulfate (CS) that possessed a higher sulfation degree than heparin. Ion pairing was exploited during multilayer formation at pH 4, while hydrogen bonding is likely to occur at pH 9. Effects of polyanions and pH value during layer formation on multilayers properties were studied by surface plasmon resonance ("dry layer mass"), quartz crystal microbalance with dissipation monitoring ("wet layer mass"), water contact angle, and zeta potential measurements. Bioactivity of multilayers was studied regarding fibronectin adsorption and adhesion/proliferation of C2C12 myoblast cells. Layer growth and dry mass were higher for both polyanions at pH 4 when ion pairing occurred, while it decreased significantly with heparin at pH 9. By contrast, CS as polyanion resulted also in high layer growth and mass at pH 9, indicating a much stronger effect of hydrogen bonding between chitosan and CS. Water contact angle and zeta potential measurements indicated a more separated structure of multilayers from chitosan and heparin at pH 4, while CS led to a more fuzzy intermingled structure at both pH values. Cell behavior was highly dependent on pH during multilayer formation with heparin as polyanion and was closely related to fibronectin adsorption. By contrast, CS and chitosan did not show such dependency on pH value, where adhesion and growth of cells was high. Results of this study show that CS is an attractive candidate for multilayer formation that does not depend so strongly on pH during multilayer formation. In addition, such multilayer system also represents a good substrate for cell interactions despite the rather soft structure. As previous studies have shown specific interaction of CS with growth factors, multilayers from chitosan and CS may be of great interest for different biomedical applications.

Nyckelord: quartz-crystal microbalance, polyelectrolyte multilayers, ionic-strength, adhesion, chitosan, films, fibronectin, fibroblasts, adsorption, integrins

Denna post skapades 2013-12-17.
CPL Pubid: 189443


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för teknisk fysik, Biologisk fysik (2007-2015)



Chalmers infrastruktur