X-ray Photoelectron Spectroscopy Surface Analysis of High Chromium Alloyed Steel Powder

Ruslan Shvab ; Eduard Hryha (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Eva Dudrova ; Ola Bergman ; Sven Bengtsson (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik)
Proc. Of 18-th International Seminar SEMDOK, Terchoca, Slovakia, 30 January-1 February 2013 p. 66-69. (2013)
[Konferensbidrag, övrigt]

The determination of the surface oxide layer composition is necessary to facilitate the adjustment of the sintering conditions for sufficient removal of the surface oxides for providing strong metal bonding between the metal particles during sintering. Investigation of the composition and thickness of the surface oxide was carried out on high Cr-alloyed water atomized steel powder. Analysis of the powder surface by X-ray photoelectron spectroscopy showed that powder particles in all cases are covered by heterogeneous oxide layer, composed of particulate features of thermodynamically stable oxides (Si-Cr-Mn) and homogeneous iron surface oxide layer in between.

Nyckelord: XPS, surface oxides, water atomized powder



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2013-12-03.
CPL Pubid: 188231

 

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)

Ämnesområden

Produktion
Hållbar utveckling
Metallurgisk processteknik
Övrig teknisk materialvetenskap

Chalmers infrastruktur