Parameters Controlling the Oxide Reduction during Sintering of Chromium Prealloyed Steel

Monika Hrubovcakova ; Eva Dudrova ; Eduard Hryha (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Margita Kabatova ; Jamila Harvanova
Advances in Materials Science and Engineering (1687-8434). (2013)
[Artikel, refereegranskad vetenskaplig]

Temperature intervals of oxide reduction processes during sintering of the Fe-3%Cr-0.5% Mo prealloyed powder using continuous monitoring of processing-exhaust gas composition (CO, CO2, and H2O) were identified and interpreted in relation to density (6.5-7.4 g/cm(3)), sintering temperature (1120 and 1200 degrees C), heating and cooling rates (10 and 50 degrees C/min), carbon addition (0.5/0.6/0.8%), type (10% H-2-N-2, N-2), and purity (5.0 and 6.0) of the sintering atmosphere. The progress in reduction processes was evaluated by oxygen and carbon contents in sintered material and fracture strength values as well. Higher sintering temperature (1200 degrees C) and density <7.0 g/cm(3) resulted in a relative decrease of oxygen content by more than 80%. The deterioration of microclimate purity of inner microvolumes of compacts shifted the thermodynamic equilibrium towards oxidation. It resulted in a closing of residual oxides inside interparticle necks. The reducing ability of the N-2 atmosphere can be improved by sintering in a graphite container. High density of 7.4 g/cm(3) achieved by double pressing indicated a negative effect on reduction processes due to restricted replenishment of the microclimate atmosphere with the processing gas. In terms of strength properties, carbon content should not be higher than similar to 0.45%.


Aricle Number: 789373

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2013-11-12. Senast ändrad 2013-12-04.
CPL Pubid: 186506


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)


Hållbar utveckling

Chalmers infrastruktur