Investigation into the growth and structure of thin-film solid solutions of iron-based superconductors in the FeSe0.92-FeSe0.5Te0.5 system

E. A. Stepantsov ; S. M. Kazakov ; V. V. Belikov ; I. P. Makarova ; R. Arpaia ; Robert Gunnarsson (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik) ; Floriana Lombardi (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik)
Crystallography Reports (1063-7745). Vol. 58 (2013), 5, p. 735-738.
[Artikel, refereegranskad vetenskaplig]

Thin films of FeSe0.92 and FeSe0.5Te0.5 iron chalcogenide superconductors and solid solutions containing these components in different ratios have been grown on the surface of LaAlO3 (102) crystals by pulsed laser deposition. Films of solid solutions have been deposited by simultaneous laser ablation from two targets of the FeSe0.92 and FeSe0.5Te0.5 stoichiometric compositions onto one substrate. An X-ray diffraction study of the film structure shows that the films grown are epitaxial and their lattice parameters regularly vary with the ratio of the deposited components, which was controllably varied by changing the ablation intensities from the targets.



Denna post skapades 2013-10-28.
CPL Pubid: 185755

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik

Ämnesområden

Fysik

Chalmers infrastruktur