Lean atmospheres for sintering chromium alloyed PM steels

Seshendra Karamchedu (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Eduard Hryha (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Sigurd Berg ; Sören Wiberg ; Lars Nyborg (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik)
Proceedings of Euro PM2013 Vol. 2 (2013), p. 353-358.
[Konferensbidrag, refereegranskat]

Hydrogen and carbon monoxide are effective reducing agents at different temperature ranges and there is only scarce experimental and theoretical data about their interaction and combined reducing effect at dry conditions and low amount. The work presents experimental and theoretical evaluation of the reducing and carburizing activity of lean nitrogen-based atmospheres containing hydrogen, carbon monoxide and small additions of hydrocarbons with their total content in the range of 0.3 to 5 vol%. Effect of carbon content (0 and 0.4 wt%) and temperature profile in the case of sintering of chromium prealloyed PM steels was evaluated. Results indicate that the carbon pickup increases with increasing CO content in the atmosphere, however it brings significant risk of oxidation. Atmospheres with low content of CO and H2 (<1.5 vol% of both) and small hydrocarbon additions showed to be good candidates for robust sintering of chromium alloyed PM steels.

Nyckelord: lean sintering atmosphere, endogas type atmospheres, carburizing, oxide reduction

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2013-10-11. Senast ändrad 2013-12-04.
CPL Pubid: 185113


Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)


Hållbar utveckling
Metallurgisk processteknik

Chalmers infrastruktur