Oxidation induced localized creep deformation in Zircaloy-2

Pia Tejland (Institutionen för teknisk fysik, Materialens mikrostruktur ) ; Hans-Olof Andrén (Institutionen för teknisk fysik, Materialens mikrostruktur )
Journal of Nuclear Materials (0022-3115). Vol. 444 (2014), 1-3, p. 30-34.
[Artikel, refereegranskad vetenskaplig]

Extensive plastic deformation in the metal underneath the oxide scale in autoclave tested Zircaloy-2 was studied using transmission electron microscopy (TEM). It was concluded that the plastic deformation is created by creep during oxidation, and is not caused by surface treatment, sample preparation or cooling from autoclave temperatures. Evidence of large strains was found in the form of dislocation tangles, dis- location patches and sub-grain formation, and also indications of twinning were found. The heavily deformed layer is around a few lm thick and no obvious difference could be seen between alloys with different strength or different oxide thickness.

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2013-10-07. Senast ändrad 2015-03-30.
CPL Pubid: 184856


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för teknisk fysik, Materialens mikrostruktur (2012-2015)


Defekter och diffusion
Metallurgi och metalliska material

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:

Microstructure Investigation of the Oxidation Process in Zircaloy-2 - The Effect of Intermetallic Particle Size