Direct measurement of bending stiffness and estimation of Young's modulus of vertically aligned carbon nanofibers

Farzan Alavian Ghavanini (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem) ; H. Jackman ; Per Lundgren (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem) ; K. Svensson ; Peter Enoksson (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem)
Journal of Applied Physics (0021-8979). Vol. 113 (2013), 19,
[Artikel, refereegranskad vetenskaplig]

The bending stiffness of individual, as-grown, vertically aligned carbon nanofibers was measured using a custom-built atomic force microscope placed inside a scanning electron microscope. The internal structure of the nanofiber was best modeled as dual-phase, composed of an inner graphitic core covered with a tapered amorphous carbon shell. It was found that the fibers have a relatively low bending stiffness, with Young's modulus values of about 10 GPa for the inner core and 65 GPa for the outer shell. The low Young's modulus of the inner core is attributed to a non-zero angle between the graphitic sheets and the nanofiber axis. The weak shear modulus between graphitic sheets thereby dominates the mechanical behaviour of the fibers.

Nyckelord: elastic-modulus, nanotubes, switches



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2013-07-01. Senast ändrad 2015-12-17.
CPL Pubid: 179585

 

Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Bionanosystem (2007-2015)

Ämnesområden

Nanovetenskap och nanoteknik
Produktion
Transport
Elektroteknik och elektronik

Chalmers infrastruktur

NFL/Myfab (Nanofabrication Laboratory)