High temperature oxidation of chromium: Kinetic modeling and microstructural investigation

Samuel Hallström ; Mats Halvarsson (Institutionen för teknisk fysik, Materialens mikrostruktur ) ; Lars Höglund ; Torbjörn Jonsson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; John Ågren
Solid State Ionics (0167-2738). Vol. 240 (2013), 0, p. 41-50.
[Artikel, refereegranskad vetenskaplig]

Using CALPHAD methods, Cr2O3 growth on pure Cr is modeled using DICTRA and the vacancy model for diffusion. The results are compared with thermobalance and TEM experiments at 625 and 700 degrees C in O-2. The experimental scatter is significant, leading to a compromise suggestion. With the experimental conditions from the furnace exposures in this work, optimized mobilities are validated with a series of oxidation simulations. Despite the complex microstructure and initial growth rate variations, it is possible to reproduce the experimental oxide thicknesses with good accuracy, allowing for extension to multicomponent systems.

Nyckelord: High temperature corrosion, Stainless steel, SEM, TEM, Kinetic parameters



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2013-05-30. Senast ändrad 2013-07-01.
CPL Pubid: 177661

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för teknisk fysik, Materialens mikrostruktur (2012-2015)
Institutionen för kemi- och bioteknik, Oorganisk miljökemi (2005-2014)

Ämnesområden

Energi
Materialvetenskap
Hållbar utveckling
Materialkemi
Metallurgi och metalliska material

Chalmers infrastruktur