Co-sintering of Solid Oxide Fuel Cells made by Aqueous Tape Casting

Johanna Stiernstedt (Institutionen för teknisk fysik) ; Elis Carlström (Institutionen för material- och tillverkningsteknik) ; Bengt-Erik Mellander (Institutionen för teknisk fysik, Fasta tillståndets fysik)
Proceedings of the 10th European SOFC Forum 2012 (2012)
[Konferensbidrag, refereegranskat]

Solid Oxide Fuel Cells (SOFC) are typically produced using organic solvent tape casting of one layer (electrolyte, anode or cathode) followed by deposition of the other layers by complex methods such as physical vapour deposition. Our aim is instead to use aqueous tape casting, followed by co-sintering. These are less costly processes, which causes less CO2-emissions, but co-sintering is a critical step. Both shrinkage and thermal expansion must be matched, and of course also the sintering temperature. Using water-based tape casting we have demonstrated co-sintering of NiO/YSZ-anode with 30% porosity and dense YSZ-electrolyte, in planar and tubular shapes. We have also shown that tape casting is a suitable prototype method for tubes. On-going work aims at increasing the porosity and decreasing the working temperature of the cell.

Nyckelord: Fuel cell, SOFC, ceramics, tape casting



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2013-03-08. Senast ändrad 2013-03-11.
CPL Pubid: 174531

 

Institutioner (Chalmers)

Institutionen för teknisk fysik (1900-2015)
Institutionen för material- och tillverkningsteknik
Institutionen för teknisk fysik, Fasta tillståndets fysik (2005-2015)

Ämnesområden

Energi
Materialvetenskap
Hållbar utveckling
Keramteknik

Chalmers infrastruktur