Long term study of Cr evaporation and high temperature corrosion behaviour of Co coated ferritic steel for solid oxide fuel cell interconnects

Jan Froitzheim (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Sead Canovic (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Maria Nikumaa (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Rakshith Nugehalli Sachitanand (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Lars-Gunnar Johansson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Jan-Erik Svensson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi)
Journal of Power Sources (0378-7753). Vol. 220 (2012), p. 217-227.
[Artikel, refereegranskad vetenskaplig]

The oxidation behaviour of the uncoated ferritic Fe-22Cr steel Sanergy HT is compared with an 640 nm Co coated version of the same material. The materials have been subject to corrosion and Cr volatilization measurements in air for up to 3000 h at 850 degrees C. Oxidation tests have been carried out both isothermal and discontinuously. The volatilization measurements were carried out using a recently developed denuder technique, which allows to quantify Cr evaporation in a time resolved manner. The oxidation process is studied from very initial phases (>15 s) to long term behaviour (3000 h). The formed oxide scales are analysed by XRD, SEM/EDX as well as TEM/EDX. The results show that both materials form an oxide scale with an inner layer of Cr2O3 and a spinel layer on top. In the case of the uncoated material, the spinel layer is of (Cr,Mn)(3)O-4 type while in the presence of a Co coating a (Co,Mn,Fe)(3)O-4 is formed. The Cr evaporation measurements show that despite the fact that the Co coating is very thin (640 nm) it effectively blocks Cr evaporation for at least 3000 h. This is in line with TEM analysis showing that after 3000 h there is only a low Cr content in the outer oxide scale. This long term stability indicates the suitability of the coated material as solid oxide fuel cell (SOFC) interconnect.

Nyckelord: SOFC, Interconnect, Cr volatilization, TEM, Corrosion, Coating

Denna post skapades 2013-01-21. Senast ändrad 2017-10-03.
CPL Pubid: 171834


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för kemi- och bioteknik, Oorganisk miljökemi (2005-2014)



Chalmers infrastruktur