Electrochemical properties of lithium polymer batteries with doped polyaniline as cathode material

J. Manuel ; Jae-Kwang Kim (Institutionen för teknisk fysik, Kondenserade materiens fysik) ; Aleksandar Matic (Institutionen för teknisk fysik, Kondenserade materiens fysik) ; Per Jacobsson (Institutionen för teknisk fysik, Kondenserade materiens fysik) ; G. S. Chauhan ; J. K. Ha ; K. K. Cho ; J. H. Ahn
Materials Research Bulletin (0025-5408). Vol. 47 (2012), 10, p. 2815-2818.
[Artikel, refereegranskad vetenskaplig]

Polyaniline (PAN!) was doped with different lithium salts such as LiPFG and LiClO4 and evaluated as cathode-active material for application in room-temperature lithium batteries. The doped PANT was characterized by FTIR and XPS measurements. In the FTIR spectra, the characteristic peaks of PANT are shifted to lower bands as a consequence of doping, and it is more shifted in the case of PANI doped with LiPFG. The cathodes prepared using PANT doped with LiPF6 and LiClO4 delivered initial discharge capacities of 125 mAh g(-1) and 112 mAh g(-1) and stable reversible capacities of 114 mAh g(-1) and 81 mAh g(-1), respectively, after 10 charge-discharge cycles. The cells were also tested using polymer electrolyte, which delivered highest discharge capacities of 142.6 mAh g(-1) and 140 mAh g(-1) and stable reversible capacities of 117 mAh g(-1) and 122 mAh g(-1) for PANT-LiPF6 and PANI-LiClO4, respectively, after 10 cycles. The cathode prepared with LiPFG doped PANT shows better cycling performance and stability as compared to the cathode prepared with LiClO4 doped PANT using both liquid and polymer electrolytes.

Nyckelord: Composites, Polymer, Electrochemical properties, Energy storage, secondary battery, electrode, films

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2013-01-17. Senast ändrad 2015-12-17.
CPL Pubid: 171198


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för teknisk fysik, Kondenserade materiens fysik (1900-2015)


Hållbar utveckling

Chalmers infrastruktur