Wear Behaviour Related to Microstructure of Ni3Al-Based Alloys

Karin Gong (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik)
Materials Research Society Symposium Proceedings Volume 980 Vol. 980 (2006),
[Konferensbidrag, poster]

A number of laboratory studies have indicated that Ni3Al-based alloys have significant potential in wear-critical applications, especially in sliding wear in a temperature range of between 400 ºC - 650 ºC. In this study, the wear behavior of an iron-alloyed Ni3Al with composition of Ni-18.8Al-10.7Fe-0.5Mn-0.5Ti-0.2B in atomic percentage and its composites reinforced by 6 vol. % Cr3C2-particles were investigated. Hot isostatic pressing (HIP) and casting processes were applied for preparing the materials. The wear rate of the tested materials under different loads and their scuffing resistance were measured by means of the Pin-on-Disk method. Analytical SEM, EDS, and XRD techniques were used to observe the microstructures and identify the phase constitutions of the materials. The tribological performance related to the analytical results revealed that the single phase Ni3Al-based alloy showed an improved scuffing resistance, compared to a duplex phase microstructure. Also, the investigation indicated that the added hard Cr-carbide played a positive role for the tribological behavior of the intermetallics, especially in terms of reducing the wear rate.

Nyckelord: Key words: Intermetallics, Nickel aluminide, Sliding wear, Wear-resistant materials, Scuffing

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2012-12-17. Senast ändrad 2014-12-19.
CPL Pubid: 167989


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)



Chalmers infrastruktur