Improvement of Mechanical Properties of Fe-Cr-Mo-[Cu-Ni]-C Sintered Sintered Steels by Sinter Hardening

E. Dudrova ; MA Grande ; M. Rosso ; M. Kabatova ; R. Bidulsky ; Eduard Hryha (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik)
Materials Science Forum (0255-5476). Vol. 672 (2011), p. 31-38.
[Artikel, refereegranskad vetenskaplig]

The effect of high temperature sintering and high cooling rate on shifting the microstructural composition to the favourably of martensite-bainite structures and thus effective improvement of mechanical properties of sintered steels based on Astaloy CrL powder with an addition of 1 and 2% Cu or 50% Distaloy AB powder and 0.65% C was investigated. All the systems were processed by both sinter-hardening and conventional sintering. The vacuum sintering at high-temperature of 1240 0C and at common temperature of 1180 0C were integrated with high (6 0C/s), medium (3 0C/s) and slow (0.1 0C/s) cooling rates; conventional sintering at 1180 0C with cooling rate of ~0.17 0C/s was carried out in a N2+10%H2 atmosphere. In dependence on chemical composition, the yield and tensile strengths of 890-1150 MPa and 913-1230 MPa respectively and impact energy of 10-15 J were achieved by sinter-hardening. The yield and tensile strengths are approximately double than those resulting from conventional sintering.

Nyckelord: Sintered steels, sinter-hardening, mechanical properties, microstructure, fractography

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2012-12-04. Senast ändrad 2013-09-23.
CPL Pubid: 167063


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)


Hållbar utveckling
Funktionella material
Övrig teknisk materialvetenskap

Chalmers infrastruktur