Ether Based Electrolyte, LiB(CN)(4) Salt and Binder Degradation in the Li-O-2 Battery Studied by Hard X-ray Photoelectron Spectroscopy (HAXPES)

R. Younesi ; M. Hahlin ; Marcel Treskow (Institutionen för teknisk fysik, Kondenserade materiens fysik) ; Johan Scheers (Institutionen för teknisk fysik, Kondenserade materiens fysik) ; Patrik Johansson (Institutionen för teknisk fysik, Kondenserade materiens fysik) ; K. Edstrom
Journal of Physical Chemistry C (1932-7447). Vol. 116 (2012), 35, p. 18597-18604.
[Artikel, övrig vetenskaplig]

Li-O-2 cells composed of a carbon cathode containing an alpha-MnO2 nanowire catalyst and a Kynar (PVDF-HFP) binder were cycled with different electrolytes containing 0.5 M LiB(CN)(4) salt in polyethylene glycol dimethyl ether (PEGDME) or tetraethylene glycol dimethyl ether (Tetraglyme) solvents. All cells exhibited fast capacity fading. To explain this, the surface chemistry of the carbon electrodes were investigated by synchrotron based hard X-ray photoelectron spectroscopy (HAXPES) using two photon energies of 2300 and 6900 eV. It is shown that the LiB(CN)(4) salt and Kynar binder were degraded during cycling, forming a layer composed of salt and binder residues on the cathode surface. The degradation mechanism of the salt differed in the two tested solvents and, consequently, different types of boron compounds were formed during cycling. Larger amounts of the degraded salt was observed using Tetraglyme as the solvent. With a nonfluorined Li-salt, the observed formation of LiF, which might be a reason for the observed blockage of pores in the cathode and for the observed capacity fading, must be due to Kynar binder decomposition. The amount of LiF formed in the PEGDME cell was larger than that formed in the Tetraglyme cell. The results indicate that not only the electrolyte solvent, but also electrolyte salt as well as the binder used for the porous cathode must be carefully considered when building a successful rechargeable Li-O-2 battery.

Nyckelord: lithium-oxygen battery, li-air cells, carbonate electrolytes, alpha-mno2, nanowires, polymer electrolyte, b(cn)(4)(-) anion, ionic liquids, graphite, stability, chemistry



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2012-10-30. Senast ändrad 2016-09-14.
CPL Pubid: 165252

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för teknisk fysik, Kondenserade materiens fysik (1900-2015)

Ämnesområden

Energi
Materialvetenskap
Transport
Kemi

Chalmers infrastruktur