ISSC committee III.2 - Fatigue and fracture

Agnes-Marie Horn ; Jonas Ringsberg (Institutionen för sjöfart och marin teknik, Marine Design) ; Shuji Aihara ; Michael Andersen ; Marco Biot ; Berend Bohlmann ; Jeroen van der Cammen ; Byung Ki Choi ; Yordan Garbatov ; Brajendra Mishra ; Xudong Qian ; Heikki Remes ; Asokendu Samanta ; Deyu Wang ; Shengming Zhang
Proceedings of the Eighteenth International Ship and Offshore Structures Congress (ISSC 2012) in Rostock, Germany, September 9-13, 2012 Vol. Vol 1 (2012), p. 365-434.
[Konferensbidrag, refereegranskat]

(COMMITTEE MANDATE) Concern for crack initiation and growth under cyclic loading as well as unstable crack propagation and tearing in ship and offshore structures. Due attention shall be paid to practical application and statistical description of fracture control methods in design, fabrication and service. Consideration is to be given to the suitability and uncertainty of physical models.

Nyckelord: Fatigue, Fracture Mechanics, Unstable Crack Propagation, Multiaxial Fatigue, Materials, Rules and Guidelines, Damage Control, Inspection and Life Extension



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2012-09-11. Senast ändrad 2012-09-11.
CPL Pubid: 163154

 

Institutioner (Chalmers)

Institutionen för sjöfart och marin teknik, Marine Design (2012-2014)

Ämnesområden

Building Futures
Materialvetenskap
Produktion
Transport
Hållbar utveckling
Innovation och entreprenörskap (nyttiggörande)
Teknisk mekanik
Farkostteknik
Annan maskinteknik
Annan materialteknik

Chalmers infrastruktur