Origin and effect of lateral cracks in oxide scales formed on zirconium alloys

Pia Tejland (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Hans-Olof Andrén (Institutionen för teknisk fysik, Mikroskopi och mikroanalys ; Institutionen för teknisk fysik, Materialens mikrostruktur )
Journal of Nuclear Materials (0022-3115). Vol. 430 (2012), 1-3, p. 64-71.
[Artikel, refereegranskad vetenskaplig]

Two varieties of Zircaloy-2, with different second phase particle (SPP) size distributions and different corrosion resistance, were oxidized in a steam autoclave. Transmission electron microscopy was used for investigation of the fine-scale lateral cracks present in the oxide scales. Crack quantification was performed and the number of cracks was correlated with the number of SPPs. A mechanism for crack formation is presented, in which the driving force is the local tensile stresses in the oxide close to the oxide/metal interface, and the initiation sites are un-oxidized SPPs located within this stress field.

Nyckelord: Zircaloy-2, lateral cracks, SPP, TEM



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2012-08-13. Senast ändrad 2015-03-30.
CPL Pubid: 161446

 

Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för teknisk fysik, Mikroskopi och mikroanalys (2005-2012)
Institutionen för teknisk fysik, Materialens mikrostruktur (2012-2015)

Ämnesområden

Energi
Materialvetenskap
Korrosionsteknik
Metallurgi och metalliska material

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:


Microstructure Investigation of the Oxidation Process in Zircaloy-2 - The Effect of Intermetallic Particle Size