Influence of the platinum-support interaction on the direct reduction of NOx under lean conditions

Filip Acke (Institutionen för oorganisk miljökemi ; Kompetenscentrum katalys (KCK)) ; Björn Westerberg (Institutionen för kemisk reaktionsteknik ; Kompetenscentrum katalys (KCK)) ; Lars Eriksson (Institutionen för teknisk kemi ; Kompetenscentrum katalys (KCK)) ; Stefan Johansson (Institutionen för teknisk fysik ; Kompetenscentrum katalys (KCK)) ; Magnus Skoglundh (Institutionen för teknisk kemi ; Kompetenscentrum katalys (KCK)) ; Erik Fridell (Institutionen för teknisk fysik, Kemisk fysik ; Kompetenscentrum katalys (KCK)) ; Gudmund Smedler (Institutionen för kemisk reaktionsteknik ; Kompetenscentrum katalys (KCK))
Studies in Surface Science and Catalysis (0167-2991). Vol. 116 (1998), p. 285-294.
[Artikel, refereegranskad vetenskaplig]

Catalysts containing Pt supported on SiC, Al2O3 and ZSM-5 were prepared and studied for NOx reduction by C3H6 in Oz excess under transient (temperature ramps) and steady-state conditions. The maximum NOx reduction activity in the heating ramp experiments was similar for Pt/SiC and Pt/ZSM-5, while Pt/Al2O3 showed higher maximum activity. Both N-2 and N2O formation was observed for all catalysts, although the respective amounts varied with the investigated system. Highest Nz selectivity was observed for Pt/Al2O3. When the NOx reduction activity was studied under steady-state conditions the activity of Pt/Al2O3 decreased substantially (mainly due to a loss in N-2 production). Pt/ZSM-5 became somewhat more selective towards Na production whereas the activity and selectivity of Pt/SiC remained at about the same values as far the heating ramp experiments. Adsorbed species on the surface of the different catalysts were investigated using in-situ FTIR in order to obtain information about the reaction mechanisms. The adsorption of species on Pt/SiC was negligible, while a number of absorption bands were observed for Pt/Al2O3 (N and C containing species, and -NCO) and Pt/ZSM-5 (HC).

Nyckelord: SELECTIVE CATALYTIC REDUCTION; EXCESS OXYGEN; NITRIC-OXIDE; CO; SPECTROSCOPY; HYDROCARBONS; ADSORPTION; STABILITY; PROPYLENE; RH/AL2O3



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2012-02-06. Senast ändrad 2012-02-14.
CPL Pubid: 154807

 

Institutioner (Chalmers)

Institutionen för oorganisk miljökemi (1900-2004)
Kompetenscentrum katalys (KCK)
Institutionen för kemisk reaktionsteknik (1972-2001)
Institutionen för teknisk kemi (1946-1998)
Institutionen för teknisk fysik (1900-2015)
Institutionen för teknisk fysik, Kemisk fysik (1900-2015)

Ämnesområden

Energi
Materialvetenskap
Nanovetenskap och nanoteknik
Transport
Hållbar utveckling
Kemiteknik

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:


Nya katalytiska material för NOx-reduktion i syreöverskott