A Phenomenological Model for the Hysteresis Behavior of Metal Sheets Subjected to Unloading/Reloading Cycles

Per-Anders Eggertsen (Institutionen för tillämpad mekanik, Material- och beräkningsmekanik) ; Kjell Mattiasson (Institutionen för tillämpad mekanik, Material- och beräkningsmekanik) ; J. Hertzman
Journal of Manufacturing Science and Engineering - Transactions of the Asme (1087-1357). Vol. 133 (2011), 6,
[Artikel, refereegranskad vetenskaplig]

The springback phenomenon is defined as elastic recovery of the stresses produced during the forming of a material. An accurate prediction of the springback puts high demands on the material modeling during the forming simulation, as well as during the unloading simulation. In classic plasticity theory, the unloading of a material after plastic deformation is assumed to be linearly elastic with the stiffness equal to Young's modulus. However, several experimental investigations have revealed that this is an incorrect assumption. The unloading and reloading stress-strain curves are in fact not even linear, but slightly curved, and the secant modulus of this nonlinear curve deviates from the initial Young's modulus. More precisely, the secant modulus is degraded with increased plastic straining of the material. The main purpose of the present work has been to formulate a constitutive model that can accurately predict the unloading of a material. The new model is based on the classic elastic-plastic framework, and works together with any yield criterion and hardening evolution law. To determine the parameters of the new model, two different tests have been performed: unloading/reloading tests of uniaxially stretched specimens, and vibrometric tests of prestrained sheet strips. The performance of the model has been evaluated in simulations of the springback of simple U-bends and a drawbead example. Four different steel grades have been studied in the present investigation.

Nyckelord: springback, elastic stiffness degradation, hysteresis effect, unloading, modulus, stress yield function, plastic-deformation, large-strain, springback, simulation, youngs modulus, steel sheet, prediction, recovery, alloy

Denna post skapades 2012-02-02.
CPL Pubid: 154726


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för tillämpad mekanik, Material- och beräkningsmekanik (2005-2017)


Teknisk mekanik

Chalmers infrastruktur