Strain Sensitivity of Carbon Nanotubes Modified Cellulose

Farshad Toomadj (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem) ; Sadia Farjana (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem) ; Anke Sanz-Velasco (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem) ; Olga Naboka (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem) ; Per Lundgren (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem) ; Katia Rodriguez ; Guillermo Toriz (Institutionen för kemi- och bioteknik, Polymerteknologi) ; Paul Gatenholm (Institutionen för kemi- och bioteknik, Polymerteknologi) ; Peter Enoksson (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem)
Procedia Engineering: 25th Eurosensors Conference; Athens; Greece; 4 September 2011 through 7 September 2011 (1877-7058). Vol. 25 (2011), p. 1353-1356.
[Konferensbidrag, refereegranskat]

Nanostructured cellulose was modified by different concentration and volume of dispersed multi-walled carbon nanotube (MWCNT) and double-walled carbon nanotube (DWCNT) solutions and its electrical properties were studied. The resulting flexible cellulose films have an electrical conductivity sensitive to changes in CNT concentration and immersion time in solution. The conductivity increases with increasing immersion time and volume and concentration of dispersed solutions; the conductivity for bacterial cellulose (BC) pellicles modified with DWCNT was increased from 0.034 S cm-1 to 0.15 S cm-1 and for BC pellicles modified with MWCNT it was increased from 0.12 S cm-1 to 1.6 S cm-1 when the immersion time was increased from 24 h to 72 h. These results are significantly higher than in previously reported work [1]. The effect of strain on the resistance during application of tensile force is shown for a simple strain gauge employing cellulose with incorporated DWCNTs. The electrical resistance of the films displays a high sensitivity to strain. It seems that this sensitivity depends on the modifying conditions, where BC pellicles which are modified in a dispersed solution with a higher concentration of CNTs show larger changes in resistance with the changes in fractional extension

Nyckelord: sensor; conductive cellulose; carbon nanotubes



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2012-01-18. Senast ändrad 2016-10-26.
CPL Pubid: 153593

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Bionanosystem (2007-2015)
Institutionen för kemi- och bioteknik, Polymerteknologi (2005-2014)

Ämnesområden

Materialvetenskap
Produktion
Transport
Elektroteknik och elektronik
Kemiteknik
Materialteknik

Chalmers infrastruktur