Texture of Electrodeposited Nanocrystalline Ni-Fe with banded structure

Uta Klement (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Mehrdad Shahabi-Navid (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Glenn Hibbard
Materials Science Forum (0255-5476). Vol. 702-703 (2012), p. 912-915.
[Artikel, refereegranskad vetenskaplig]

Optical microscopy on the etched cross-section of a nanocrystalline Ni-18 wt.% Fe electrodeposit revealed the existence of a banded structure perpendicular to the growth direction. To evaluate if the banded structure is affecting grain growth and texture development, EBSD orientation maps were obtained after annealing for 30 min at 300, 350, and 400°C. Grown grains were found to be random in shape and no preferential sites for grain growth were observed. The texture of the grown grains is changing upon annealing and the final <111> fibre texture parallel to growth direction of the electrodeposit can be obtained from texture components found at lower annealing temperatures when performing one or two consecutive twinning operations.

Nyckelord: Ni-Fe, electroplating, nanocrystalline material, banded structure, EBSD, annealing



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2011-11-29. Senast ändrad 2015-05-07.
CPL Pubid: 149200

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)

Ämnesområden

Materialvetenskap
Materialteknik

Chalmers infrastruktur