Microstructure characterization of white layer formed by hard turning and wire electric discharge machining in high carbon steel (AISI 52100)

Seyed Hosseini B. (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Uta Klement (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Jacek Kaminski (Institutionen för material- och tillverkningsteknik, Tillverkningsteknik)
Advanced Materials Research (1022-6680). Vol. 409 (2012), p. 684-689.
[Artikel, refereegranskad vetenskaplig]

White layers, formed during hard turning and wire electric discharge machining, were characterized by means of X-ray diffraction, scanning electron microscopy and transmission electron microscopy. Different cutting speeds and flank wear were utilized in order to obtain different thermally and/or plastically deformed white layer. Since the white layer after wire electric discharge machining is mainly thermally induced, it was used as a reference structure. In the investigation, both bainitic and martensitic structures were studied. With a constant flank wear of 0.175 mm the thickness of the white layer increased from 1.5 μm to 3 μm as the cutting speed was increased. In both processes the white layer were characterized by nano-sized grains and surface tensile residual stresses. M3C carbides were observed in the hard turned white layer, indicating that the time and temperature needed for completely dissolving the carbides were not reached during cutting. For both materials the white layers formed by wire electric discharge machining consisted of ~ 30 vol. % of retained austenite. Observation regarding the volume fraction of the retained austenite in the white layer formed by hard turning for martensitic material showed an increase in the volume fraction of retained austenite from ~ 2 - 3 vol. % to ~ 6 vol. %, while this observation was not seen in the white layer formed in the bainitic material.

Nyckelord: White layer, Hard Turning, Wire Electric Discharge Machining (WEDM), XRD, TEM

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2011-11-28. Senast ändrad 2016-11-02.
CPL Pubid: 149028


Läs direkt!

Länk till annan sajt (kan kräva inloggning)