Structural design and properties of hydrogel biomaterials

Mikael Larsson (Institutionen för kemi- och bioteknik, Farmaceutisk teknologi ; SuMo Biomaterials)
2011. ISBN: 978-91-7385-592-1.- 63 s.
[Doktorsavhandling]

Today a range of materials are used in medical applications; such materials are collectively denoted as biomaterials. A special class of biomaterials currently given much scientific interest is hydrogels. In particular a contemporary research topic is to create multicomponent materials in which synergetic effects are achieved. The works this thesis is based on aimed to create new potential multicomponent hydrogel biomaterials, where the presented materials can be divided into three groups: superabsorbents (SAPs), films with tuneable permeability and systems with inducible gelation. The materials were characterized with regard to macroscopically observed properties of importance for material performance. Based on observed properties, components in the materials and material structures conclusions were drawn about important structural design characteristics. Polyacrylic acid (PAA) based SAPs, in which microfibrillated cellulose (MFC) was used as a filler material, were synthesized. For the investigated SAPs some MFC was found to be equivalent to the same mass of traditional crosslinker with regard to modifying equilibrium swelling and shear modulus. Furthermore, the resistance to fracture upon compression was improved for MFC containing gels. Films composed of MFC and the water soluble polymer hydroxypropyl methylcellulose (HPMC) were prepared. The water permeability of the films displayed a dependence on HPMC content opposite of what is commonly expected. The films exhibited large, close to one-dimensional, swelling. Also, films composed of crosslinked polydimethylsiloxanes (PDMS) and carbomer micro particles (PAA based) or sucrose were synthesized. The permeability of water vapour through those films was tuneable by the addition of carbomer, but not by addition of sucrose. This was explained by that the swollen carbomer retained open channels with high diffusion in the films. In contrast, the highly elastic and hydrophobic PDMS probably sealed the pores left by dissolved sucrose. Gels based on nanocapsules of carboxymethyl-hexanoyl chitosan (CHC) with in situ gelling capability were found to have properties making them highly promising for biomedical, and in particular drug delivery applications. Hopefully the presented materials will act as inspiration for structural design, contribute to the understanding of structure-properties correlations and perhaps even contribute to improvement of people’s quality of life through new products reaching the market.

Nyckelord: Biomaterials, Chitosan, Drug release, Hydrogels, Mechanical properties, Microfibrillated cellulose, Polyacrylic acid, Swelling



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2011-11-16. Senast ändrad 2016-04-04.
CPL Pubid: 148607

 

Institutioner (Chalmers)

Institutionen för kemi- och bioteknik, Farmaceutisk teknologi (2005-2014)
SuMo Biomaterials

Ämnesområden

Materialvetenskap
Fysikalisk kemi
Materialteknik
Galenisk farmaci

Chalmers infrastruktur

Relaterade publikationer

Inkluderade delarbeten:


High Performance Polysodium Acrylate Superabsorbents Utilizing Microfibrillated Cellulose to Augment Gel Properties


Different types of microfibrillated cellulose as filler materials in polysodium acrylate superabsorbents


A novel dual-structure, self-healable, polysaccharide based hybrid nanogel for biomedical uses


Increased water transport in PDMS silicone films by addition of excipients


Examination

Datum: 2011-12-16
Tid: 10:00
Lokal: KB-Salen, Kemigården 4, Chalmers University of Technology
Opponent: Dr. Oguz Okay, Professor, Istanbul Technical University

Ingår i serie

Doktorsavhandlingar vid Chalmers tekniska högskola. Ny serie