Delubrication of PM Components Based on Cr-Prealloyed Steel Powder – Chances and Risks

Eduard Hryha (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Seshendra Karamchedu (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Lars Nyborg (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik)
Proc. of EURO PM2011 Congress & Exhibition, 9-12 October 2011, Barcelona, Spain Vol. 3 (2011), p. 105-110.
[Konferensbidrag, refereegranskat]

Utilization of prealloyed powder grades for production of high-performance PM structural parts require reconsidering of specific stages of sintering process like debinding. Modern lubricants are complex organic compounds, decompositions of which leads to production of a number of species – from complex hydrocarbons to carbon oxides. Composition and amount of decomposition products are strongly determined by the temperature profile and processing atmosphere composition/purity. Uncontrolled delubrication process, especially in the case of the PM components containing elements with high-sensitivity to oxygen, can lead to considerable oxidation. Therefore, in-situ monitoring of the processing parameters during delubrication is presented utilizing commonly used in industry sensors (dew-point, CO2 and O2). Delubrication was monitored in a number of inert and reducing gases of the different purity. Based on the specimens analysis and gas monitoring profiles it is recommended to perform delubrication at the temperatures below 500°C in dry inert atmospheres in the case of ethylenbisstearamide-based lubricants.

Nyckelord: delubrication, sintering atmosphere, processing atmosphere control, alloyed sintered steels

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2011-10-19.
CPL Pubid: 147451


Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)


Hållbar utveckling
Funktionella material
Övrig teknisk materialvetenskap

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:

Delubrication of Chromium Prealloyed Powder Metallurgy Steels

Critical Aspects of Delubrication and Sintering of Chromium-alloyed Powder Metallurgy Steels