On the mechanism of enhanced photocatalytic activity of composite TiO(2)/carbon nanofilms

Raja Sellappan (Institutionen för teknisk fysik, Kemisk fysik) ; A. Galeckas ; V. Venkatachalapathy ; A. Y. Kuznetsov ; Dinko Chakarov (Institutionen för teknisk fysik, Kemisk fysik)
Applied Catalysis B-Environmental (0926-3373). Vol. 106 (2011), 3-4, p. 337-342.
[Artikel, refereegranskad vetenskaplig]

In the search for the origin of the enhanced photocatalytic activity of composite TiO(2)-carbon systems, we have fabricated and analyzed well-defined model samples consisting of anatase and graphitic carbon with and without modifying the interface between them by a thin SiO(2) space layer. The films with a TiO(2)/C interface show noticeably lower photoluminescence intensity and shorter carrier life times compared to single TiO(2) films with the same thickness and composition. The stronger non-radiative recombination is mainly assigned to charge carrier leakage (transfer) at the interface between TiO(2) nanocrystallites and the carbon film. (C) 2011 Elsevier B.V. All rights reserved.

Nyckelord: Photocatalysis, TiO(2)-carbon composites, Photoluminescence, Charge, carriers lifetime, Charge transfer mechanism, anatase tio2, carbon, photoluminescence, luminescence, arrays, water, spectroscopy, excitation



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2011-09-29. Senast ändrad 2011-10-05.
CPL Pubid: 146719

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för teknisk fysik, Kemisk fysik (1900-2015)

Ämnesområden

Materialvetenskap
Nanovetenskap och nanoteknik
Fysik

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:


MECHANISMS OF ENHANCED ACTIVITY OF MODEL TiO2/CARBON and TiO2/METAL NANOCOMPOSITE PHOTOCATALYSTS