Influence of shot peening on fatigue durability of decarburized spring steels

Kamellia Dalaei (Institutionen för material- och tillverkningsteknik) ; Jonas Höijer ; Gunnar Åkerström ; Birger Karlsson (Institutionen för material- och tillverkningsteknik)
Proceeding of international shot peening conference (ICSP 11) p. 183-188. (2011)
[Konferensbidrag, refereegranskat]

The influence of shot peening on high cycle fatigue behaviour of spring steel was investi-gated. The material studied was a quenched and tempered carbon steel 51SiCr7 (0.55 C, 1.9 Si and 0.9 Mn). Three series of fatigue specimens with zero, 0.15 and 0.45 mm depth of decarburization were produced. Half of the specimens from each series were shot peened, leading to a thickness of the compressed surface layer of about 0.25 mm. The specimens were tested in bending fatigue. A 45% improvement in fatigue limit of the decarburized series was achieved after shot peening. The detail of relaxation of the residual stresses was followed and compared for different series of specimens.

Nyckelord: Decarburization, fatigue strength, residual stresses, shot peening

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2011-09-28.
CPL Pubid: 146673


Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik (2005-2017)


Funktionella material

Chalmers infrastruktur