Oxidation behaviour of a Mo(Si,Al)2 based composite at 1500 degrees C

Linda Ingemarsson (Institutionen för kemi- och bioteknik) ; Kristina Hellström (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Lars-Gunnar Johansson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Jan-Erik Svensson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Mats Halvarsson (Institutionen för teknisk fysik, Mikroskopi och mikroanalys)
Intermetallics (0966-9795). Vol. 19 (2011), 9, p. 1319-1329.
[Artikel, refereegranskad vetenskaplig]

The oxidation of a Mo(Si,Al)(2) composite is investigated at 1500 degrees C in dry air using exposure times from 1 to 1000 h. Cross sections are examined with Scanning Electron Microscopy (SEM) and the phase composition is analyzed by X-ray diffraction (XRD). The material forms a continuous and protective alumina layer, the growth of the alumina layer following parabolic kinetics. Immediately below the scale Mo(Si,Al)(2) is replaced by a Mo(5)(Si,Al)(3) layer due to the flux of aluminum to the scale. The Al concentration in the Mo(Si,Al)(2) phase in the underlying substrate decreases from 27% before exposure to 16-17% after 1000 h. The continuous alumina layer becomes covered by a top layer consisting of alumina grains embedded in a viscous melt with approximate composition 7 Na(2)O-15 Al(2)O(3)-78 SiO(2). With time, sodium is volatilized from the melt and the top scale layer transforms to a mixture of alumina, mullite and silica melt.

Nyckelord: Molybdenum silicides, Multiphase intermetallics, Oxidation, Microstructure, Electron microscopy, scanning, high-temperature oxidation, (mo,w)si-2-based composite, molybdenum, disilicide, intermetallic alloys, mosi2, al, intermediate, atmospheres, resistance, silicides, kamey cg, 1992, v7, p2747



Denna post skapades 2011-08-10. Senast ändrad 2015-02-11.
CPL Pubid: 143943

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kemi- och bioteknik (2005-2014)
Institutionen för kemi- och bioteknik, Oorganisk miljökemi (2005-2014)
Institutionen för teknisk fysik, Mikroskopi och mikroanalys (2005-2012)

Ämnesområden

Materialteknik

Chalmers infrastruktur