Metallurgical Response of Electron Beam Welded Allvac® 718Plus™

Joel Andersson (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Göran Sjöberg (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Hannu Hänninen
Hot Cracking Phenomena in Welds III, Ed. by T.H. Boellinghaus, J.C. Lippold, and C.E. Cross p. 415-428. (2011)
[Konferensbidrag, refereegranskat]

Electron beam welding of forged Allvac 718Plus superalloy has been carried out without any visible cracks in weld cross-sections. Healed cracks in the heat affected zone were, however, seen in most cross-sections with the healing as well as the cracking believed to be due to the constitutional liquation of the δ-phase. The δ-phase undergoes constitutional liquation in the Heat Affected Zone (HAZ) and consequently decreases the ductility of the material and renders cracks in the HAZ but due to the large amount of eutectic liquid produced at the same time the healing of the opened cracks takes place.

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2011-05-05. Senast ändrad 2017-02-07.
CPL Pubid: 140311


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)


Övrig teknisk materialvetenskap

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:

Weldability of Precipitation Hardening Superalloys – Influence of Microstructure