Oxidation of Ti2AlC bulk and spray deposited coatings

Marie Sonestedt (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; J. Frodelius ; M. Sundberg ; L. Hultman ; Krystyna Stiller (Institutionen för teknisk fysik, Mikroskopi och mikroanalys)
Corrosion Science (0010-938X). Vol. 52 (2010), 12, p. 3955-3961.
[Artikel, refereegranskad vetenskaplig]

The oxidation behaviour of Ti2AlC bulk and high velocity oxy-fuel spray deposited coatings has been investigated for temperatures up to 1200 degrees C. X-ray diffraction and electron microscopy show that bulk Ti2AlC forms a continuous layer of alpha-Al2O3 below a layer of TiO2 at temperatures as low as 700 degrees C. Oxidation of the Ti2AlC coatings is more complex, and also involves the phases Ti3AlC2, TiC, and TixAly, formed during the spraying process. alpha-Al2O3 is observed, however, it is unevenly distributed deep into the material, and does not form a continuous layer essential for good oxidation resistance.

Nyckelord: Aluminium, Ceramic, Titanium, SEM, XRD, Oxidation, high-temperature, m(n+1)ax(n) phases, alumina, alloys, ceramics, behavior, films, air

Denna post skapades 2010-12-13. Senast ändrad 2012-02-17.
CPL Pubid: 130665


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för teknisk fysik, Mikroskopi och mikroanalys (2005-2012)



Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:

Microstructure and properties of coatings produced by spray deposition of Ti2AlC powders