Quantification of the cold worked material inside the deep honing grooves on cylider liner surfaces and its effect on wear

Zlate Dimkovski (Institutionen för material- och tillverkningsteknik, Tillverkningsteknik) ; Cecilia Anderberg (Institutionen för material- och tillverkningsteknik, Tillverkningsteknik) ; Bengt-Göran Rosén (Institutionen för material- och tillverkningsteknik, Tillverkningsteknik) ; Robert Ohlsson ; Tom Thomas
Wear (0043-1648). Vol. 267 (2009), 12, p. 2235-2242.
[Artikel, refereegranskad vetenskaplig]

The increased presence of cold work material on cylinder liners due to the introduction of the diamond honing is undesirable as it seats the oil-bearing honing grooves. The most of it is a smeared metal inside the deep honing grooves (blechmantel) that may break and act as abrasive wear particles increasing the bore wear. An attempt has been made to estimate the extent of removal of blechmantel for different wear regimes present at the middle and top region (near the top dead centre) of the liner surface using the least worn bottom region as a reference for comparison. A number of truck grey iron cylinder liners were axially sectioned after varying periods of engine running under similar conditions of load, engine speed and lubrication. 3D surface measurements were taken at the three regions and a range of standard parameters was extracted. Combining the profile and image analysis, an algorithm was developed to identify and quantify the blechmantel. The algorithm has successfully identified/quantified the blechmantel and can be used for automatic surface quality and process control. It was found that the amount of the blechmantel in the middle section was approximately the same (though slightly lower) as that in the bottom section, while there was a considerable dislocation and removal of blechmantel in the top section and thereby it represents one of the possible causes for wear. Axial wear scratches of different size and distribution were observed not only through the whole stroke area, but also in the bottom region. All engines and liners performed well throughout the tests, and the observed quantities of blechmantel and axial scratches are acceptable for the time being.

Nyckelord: Cold work quantification; Cylinder liner wear; Surface topography; Engine tests; Diamond honing



Denna post skapades 2010-11-02. Senast ändrad 2013-10-29.
CPL Pubid: 128463

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Tillverkningsteknik

Ämnesområden

Materialteknik

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:


Surfaces of Honed Cylinder Liners