Structural effects on thermal properties and morphology in XLPE

Susanne Nilsson (Institutionen för kemi- och bioteknik, Teknisk ytkemi) ; Thomas Hjertberg ; Annika Smedberg
European Polymer Journal (0014-3057). Vol. 46 (2010), 8, p. 1759-1769.
[Artikel, refereegranskad vetenskaplig]

This study investigated the morphological, thermal and mechanical changes with increasing crosslink density for two low density polyethylenes (LDPE). A reference LDPE was compared with an LDPE containing a higher number of vinyl groups that was introduced via a copolymerisation with a diene. During crosslinking, two reactions simultaneously occur in the copolymer, i.e. a reaction of the vinyl groups and combination crosslinking. After crosslinking with a low amount of peroxide, the majority of the crosslinks originate from reacted vinyl groups in the LDPE containing the higher number of vinyl groups, whereas the crosslinks in the reference LDPE originate from combination crosslinking, thus leading to different crosslinked structures for the two polymers. The melt temperature, crystallisation temperature, and degree of crystallinity were measured using a Differential Scanning Calorimeter. Thermal fractionation studies and morphology studies were also made. The Differential Scanning Calorimetry results show a decrease in those properties for both materials along with a concurrent change in the morphology when the crosslink density increased. The results deviate slightly between the materials.

Nyckelord: Low density polyethylene, Crosslinking, Morphology, Crosslinked polyethylene



Denna post skapades 2010-10-01. Senast ändrad 2016-12-05.
CPL Pubid: 127149

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kemi- och bioteknik, Teknisk ytkemi (2005-2014)

Ämnesområden

Polymerkemi
Kemiteknik

Chalmers infrastruktur