Dry densification of carbon nanotube bundles

Teng Wang (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem) ; Kjell Jeppson (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem) ; Johan Liu (Institutionen för mikroteknologi och nanovetenskap, Bionanosystem)
Carbon (0008-6223). Vol. 48 (2010), 13, p. 3795-3801.
[Artikel, refereegranskad vetenskaplig]

A dry method for densifying vertically aligned carbon nanotube bundles is proposed and experimentally validated. The process uses the deposition of thin SiO2 films to seal the porous CNT bundles at low pressure. When the CNT bundles are transferred back to ambient pressure they are densified by the pressure difference obtained between the inner and outer sides of the thin film. The effects of the densification have been studied for different thicknesses of SiO2 films deposited by two different deposition techniques. The diameters of the narrowest densified sections are 26 +/- 3% of their original sizes after dry densification by 50 nm thick SiO2. The proposed dry densification method is also compared to existing liquid-based methods and its limitations are discussed. (C) 2010 Elsevier Ltd. All rights reserved.

Nyckelord: chemical-vapor-deposition, growth, fabrication, membranes, films, dense



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2010-09-10. Senast ändrad 2011-01-10.
CPL Pubid: 126031

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Bionanosystem (2007-2015)

Ämnesområden

Nanovetenskap och nanoteknik
Elektroteknik och elektronik
Elektronik

Chalmers infrastruktur