Microwave absorbing properties of structural nanocomposites with surface treated Co ferrite nanoparticles as filler

A. Jänis ; R.T. Olsson ; S.J. Savage ; Uta Klement (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik)
Proceedings of SPIE - The International Society for Optical Engineering (0277-786X). Vol. 7644 (2010),
[Konferensbidrag, övrigt]

An analysis of the microwave absorbing properties of several polymer-(epoxy) based nanocomposites is presented. The nanoparticles of interest for this study were cobalt ferrite nanoparticles. For better dispersion of the nanoparticles in the polymer matrix surface treatment of the nanoparticles with silane compounds was performed. The nanoparticles were surface-treated with 3-glycidoxypropyl- (GPTMS), aminopropyl- (APTMS) or methyl-silsesquioxane (MTMS). The nanoparticles with GPTMS-coating dispersed well in epoxy without sedimentation while the other nanoparticles formed agglomerates in epoxy. The GPTMS-based composites showed higher fracture toughness than the MTMS-based composites. The microwave properties, permittivity and permeability, of GPTMS-based composites were measured in the frequency range between 3.95 GHz and 18 GHz and showed no influence of surface treatment on permeability.

Nyckelord: Absorption properties, Ferrites, Microwaves, Nanocomposites, Silane, Surface treatment



Denna post skapades 2010-07-05. Senast ändrad 2015-07-01.
CPL Pubid: 123696

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)

Ämnesområden

Materialteknik

Chalmers infrastruktur