Low cycle fatigue and deformation behaviour of austenitic manganese steel in rolled and as-cast conditions

Martin Schilke (Institutionen för material- och tillverkningsteknik, Materialteknologi) ; Johan Ahlström (Institutionen för material- och tillverkningsteknik, Materialteknologi) ; Birger Karlsson (Institutionen för material- och tillverkningsteknik, Materialteknologi)
Procedia Engineering (1877-7058 ). Vol. 2 (2010), 1, p. 623-628.
[Konferensbidrag, refereegranskat]

This paper presents a characterisation of two austenitic manganese (~12-13 wt%) rail steels, one in rolled (Mn13(R)) and the other in as-cast (Mn13(C)) condition. Cyclic and monotonic behaviour as well as hardness and microstructure have been investigated. The results do not show any major difference between the materials, but comparison with literature reveals large differences compared to pearlitic and bainitic rail steels. The manganese steels are softer initially and harden during cyclic and monotonic loading.

Nyckelord: Austenitic manganese steel; TWIP steel; low cycle fatigue; deformation behaviour; railway rail steel



Denna post skapades 2010-06-14. Senast ändrad 2014-09-02.
CPL Pubid: 122745

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Materialteknologi

Ämnesområden

Materialteknik

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:


Comparability of Railway Rail Steels Low Cycle Fatigue Behaviour