Water-Based Latex Dispersions. 5: NMR Relaxation Studies of Deuterium Labeled Nonylphenol Ethoxylate

Catherine Boissier (Institutionen för kemi- och bioteknik) ; Krister Holmberg (Institutionen för kemi- och bioteknik, Teknisk ytkemi) ; Jan-Erik Löfroth (Institutionen för kemi- och bioteknik, Teknisk ytkemi) ; Magnus Nydén (Institutionen för kemi- och bioteknik, Teknisk ytkemi ; SuMo Biomaterials)
Journal of Dispersion Science and Technology (0193-2691). Vol. 30 (2009), 6, p. 873-880.
[Artikel, refereegranskad vetenskaplig]

The dynamics and conformation of the nonionic surfactant NP100 (nonylphenol ethoxylate with an average of 84 oxyethylene units), adsorbed on colloidal silica and on polystyrene latex particles, have been studied by the nuclear magnetic resonance relaxation technique. To obtain specific information about the spin relaxation from the methylene groups situated at the hydroxyl-terminal end of the polyoxyethylene (POE) chain, this part was labeled with deuterium in a two-step synthesis. Spin relaxation studies of the labeled part of the adsorbed surfactant (2H relaxation) suggested that the dynamics was slower in comparison with the spin relaxation of the surfactant in solution. Also, it was seen that the dynamics was slower on the silica surface than on the polystyrene surface. This was in agreement with previous studies on the average proton spin relaxation of the whole POE chain of the surfactant on silica and on polystyrene surfaces. The correlation time constant for the slow motions of the POE chain was calculated to be as large as 7.4 ms for NP100 on the polystyrene particles. Also this was in good agreement with studies made on the exchange dynamics of the surfactant in different dispersions, where it was found that the exchange between the solution and the particles was slow.

Nyckelord: 2H relaxation, nonylphenol ethoxylate, nuclear magnetic resonance, (NMR), polystyrene, silica, nuclear-magnetic-resonance, different interfacial properties, atomic-force microscopy, film formation, nonionic surfactants, colloidal particles, adsorption, dynamics, layers, ether

Denna post skapades 2010-02-23. Senast ändrad 2016-04-19.
CPL Pubid: 114140


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för kemi- och bioteknik (2005-2014)
Institutionen för kemi- och bioteknik, Teknisk ytkemi (2005-2014)
SuMo Biomaterials


Yt- och kolloidkemi

Chalmers infrastruktur