Magnesium diboride nanobridges fabricated by electron-beam lithography

Anayesu Malisa (Institutionen för mikroteknologi och nanovetenskap) ; Serge Charlebois (Institutionen för mikroteknologi och nanovetenskap) ; Tobias Lindström (Institutionen för mikroteknologi och nanovetenskap)
Journal of Applied Physics (00218979 ). Vol. 98 (2005), 12, p. 1-5.
[Artikel, refereegranskad vetenskaplig]

MgB2 nanobridges were fabricated by e-beam lithography and Ar-ion beam milling. Nanobridges of widths ranging from 60 nm to 1 μm and 3 μm in length were realized by Ar-ion beam milling using amorphous carbon as etching mask. The processing did not harm the superconducting properties appreciably. High values of the critical current density, more than 10 MA cm2, were measured for bridges with widths down to 60 nm. Current-voltage (I-V) characteristics showed a behavior typical of a bridge going normal, after the critical current is exceeded, and remaining normal as the current is decreased to a lower switch back value due to Joule heating. We could also observe switching behavior in some bridges indicating formation of normal hotspots in the bridges before they returned to their superconducting state. Alternative explanations may include natural grain boundaries in the film or the movement of Abrikosov vortices. The current-voltage (I-V) characteristics showing critical current densities up to 5× 107 A/cm2 indicates excellent film properties in the nanobridges.



Denna post skapades 2010-01-22.
CPL Pubid: 110325

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap

Ämnesområden

Teknisk fysik

Chalmers infrastruktur